Semi Conductive Thickness 0.25mm Water Blocking Tape Manufactured in China

1.Color: Black 2.Material: Yarn 3.Thickness: 0.1mm-0.5mm 4.Tensile Strength: More Than 18n/Cm 5.Elong-Ation: More Than 12% 6.Short Term Stability: 230 Celsius Degrees

Inquiry Now

Product Description

Product Description

Basic Info.

1	Model NO.	Insulation
2	Long Term Stability	90 Celsius Degrees
3	Moisture Conten	Less Than 6%
4	Type	Insulation Tape
5	Chemistry	Waterproof
6	Transport Package	Wood Package
7	Specification	Customized

Application

It is a combination of tape, yarn, or coating to prevent longitudinal penetration of water into the cable core .The main principle is to use a kind of polymer that can absorb water and quickly form gel to fill the seepage channel through the expansion of hydrogel. It is widely usedIn optical fiber cable, data cable, telecom cable and control cable.

Feature

1.Proven high performance of swelling and water blocking
2.Process friendly
3.REACH and RoHS compliant

Package
In Roll ID 76mm-105mm

Technical Parameter
Single Side Non-conductivity

Thickness	Mass Per Area	Tensile Strength	Elong- Ation	Swelling Speed	Swelling Height	Short Term Stability	Long Term Stability	Moisture Content
mm	g/m2	N/cm	%	mm/1,0	mm/3,0	ºC	ºC	%
0.1±0.01	40±5	≥18	≥12	≥3	≥4	230	90	≤6
0.15±0.03	60±5	≥20	≥12	≥5	≥8	230	90	≤6
0.18±0.03	65±5	≥25	≥12	≥6	≥9	230	90	≤6
0.20±0.03	70±10	≥30	≥12	≥12	≥12	230	90	≤6
0.25±0.03	80±10	≥30	≥12	≥12	≥12	230	90	≤6
0.30±0.03	90±10	≥35	≥12	≥12	≥12	230	90	≤6

Double Side Non-conductivity

Thickness	Mass Per Area	Tensile Strength	Elong- Ation	Swelling Speed	Swelling Height	Short Term Stability	Long Term Stability	Moisture Content
mm	g/m2	N/cm	%	mm/1,0	mm/3,0	ºC	ºC	%
0.18±0.01	65±10	≥25	≥12	≥4	≥6	230	90	≤6
0.20±0.03	70±10	≥28	≥12	≥6	≥9	230	90	≤6
0.25±0.03	80±10	≥35	≥12	≥8	≥12	230	90	≤6
0.30±0.03	90±10	≥40	≥12	≥10	≥14	230	90	≤6
0.35±0.03	100±10	≥40	≥12	≥10	≥14	230	90	≤6
0.20±0.03	75±10	≥35	≥12	≥10	≥12	230	90	≤6
0.25±0.03	85±10	≥35	≥12	≥12	≥15	230	90	≤6
0.50±0.03	130±10	≥45	≥12	≥12	≥16	230	90	≤6

Single Side Semi-conductivity

Thickness	Mass Per Area	Tensile Strength	Elong- Ation	Swelling Speed	Swelling Height	Surface Resistance	Volume Resistance	Moisture Content
mm	g/m2	N/cm	%	mm/1,0	mm/3,0	Ω	Ω.cm	%
0.25±0.03	90±5	≥25	≥12	≥6	≥8	≤1500	<1x10(6)	≤9
0.30±0.03	100±5	≥30	≥12	≥8	≥12	≤1500	<1x10(6)	≤9
0.35±0.03	110±5	≥35	≥12	≥10	≥14	≤1500	<1x10(6)	≤9
0.40±0.03	130±10	≥40	≥12	≥11	≥15	≤1500	<1x10(6)	≤9
0.45±0.03	140±10	≥45	≥12	≥12	≥16	≤1500	<1x10(6)	≤9
0.50±0.03	160±10	≥50	≥12	≥12	≥18	≤1500	<1x10(6)	≤9
Short Term Stability:230ºCLong Term Stability: 90C,

Double SideSemi-conductivity

Thickness	Mass Per Area	Tensile Strength	Elong- Ation	Swelling Speed	Swelling Height	Surface Resistance	Volume Resistance	Moisture Content
mm	g/m2	N/cm	%	mm/1,0	mm/3,0	Ω	Ω.cm	%
0.25±0.03	100±5	≥30	≥12	≥7	≥10	≤1500	<1x10(6)	≤9
0.30±0.03	110±5	≥30	≥12	≥8	≥12	≤1500	<1x10(6)	≤9
0.35±0.03	120±5	≥35	≥12	≥9	≥13	≤1500	<1x10(6)	≤9
0.40±0.03	130±10	≥40	≥12	≥10	≥14	≤1500	<1x10(6)	≤9
0.50±0.03	130±10	≥50	≥12	≥12	≥16	≤1500	<1x10(6)	≤9
0.50±0.03	160±10	≥50	≥12	≥13	≥18	≤1500	<1x10(6)	≤9
Short Term Stability(C):230 Long Term Stability: 90C,